I am rebuilding a Toyota 1ZZ engine. It has Torque to Yield main bolts. What do I do about checking main clearances? Will they close up with new bolts? Can NEW TTY bolts be reused? Buy 2 sets of TTY bolts ($37 per set)? Spring for ARP bolts ($115)? I am not opposed to the ARP but this issue will surface again, and some folks aren't gonna want to spring for the ARP stuff.
thanks,
Lewy
thanks,
Lewy
-
- HotPass
- Posts: 9393
- Joined: Tue Nov 22, 2005 5:41 am
- Location:
Re: Torque To Yield
https://www.svtperformance.com/threads/ ... ts.894486/
https://www.onallcylinders.com/2017/03/ ... need-know/
https://www.onallcylinders.com/2017/03/ ... need-know/
Driving Force Online: BREAKING NEWS—Ohio Governor Signs SEMA-Supported Vehicle Freedom Bill Into Law!
-
- Pro
- Posts: 414
- Joined: Sat Aug 23, 2008 7:12 am
- Location:
Re: Torque To Yield
How it works:
In a typical bolt the underhead radius sees a significant stress concentration. TTY actually causes the material in that radius to yield. If you then removed the bolt and could look inside you will find residual compressive stress in that radius, not unlike rolled fillets in a crankshaft.
TTY takes advantage of this. After assembly and in service parts settle and the bolt tension drops a bit. What this does is keep cyclic stresses in the underhead radius below the fatigue limit while maximizing the overall fastener tension. I expect the OEMs have done a lot of testing to refine the design.
Pressure vessel manufacture uses a similar idea. Fill the vessel with water and pump it up until it yields just a bit. This washes out left over stresses from welding and fabrication with result of a more fatigue resistant vessel in service.
That said, maybe it's fine but I personally would be hesitant to reuse TTY after in service. I like the suggestion to use old bolts for mockup then new ones for final assembly.
In a typical bolt the underhead radius sees a significant stress concentration. TTY actually causes the material in that radius to yield. If you then removed the bolt and could look inside you will find residual compressive stress in that radius, not unlike rolled fillets in a crankshaft.
TTY takes advantage of this. After assembly and in service parts settle and the bolt tension drops a bit. What this does is keep cyclic stresses in the underhead radius below the fatigue limit while maximizing the overall fastener tension. I expect the OEMs have done a lot of testing to refine the design.
Pressure vessel manufacture uses a similar idea. Fill the vessel with water and pump it up until it yields just a bit. This washes out left over stresses from welding and fabrication with result of a more fatigue resistant vessel in service.
That said, maybe it's fine but I personally would be hesitant to reuse TTY after in service. I like the suggestion to use old bolts for mockup then new ones for final assembly.
Re: Torque To Yield
Yes, just use the old TTY bolts for clearance checking, then use the new TTY bolts for final assembly.
-
- Guru
- Posts: 9633
- Joined: Tue Nov 27, 2007 9:27 am
- Location: Chicago
- Contact:
Re: Torque To Yield
By definition, a bolt should be torqued into its elastic range but not into its plastic range.
If within its elastic range,the bolt should return to its original length. If it does not, it's use is
problematic.
Some OEMs will specify a used bolt critical dimension; either length or diameter, within which the bolt
may be reused. Lacking specifics, I find it useful to carefully measure and compare a new bolt to a used bolt.
Sometimes, the bolt stretch occurs in the threaded area which is more difficult to measure. Running a new nut down the bolt to test for thread binding can often indicate thread stretch.
Beware of using bolts that are too high in grade for the application. If they cannot be properly stretched into their elastic range, they will not hold, no matter how strong they are advertised.
If within its elastic range,the bolt should return to its original length. If it does not, it's use is
problematic.
Some OEMs will specify a used bolt critical dimension; either length or diameter, within which the bolt
may be reused. Lacking specifics, I find it useful to carefully measure and compare a new bolt to a used bolt.
Sometimes, the bolt stretch occurs in the threaded area which is more difficult to measure. Running a new nut down the bolt to test for thread binding can often indicate thread stretch.
Beware of using bolts that are too high in grade for the application. If they cannot be properly stretched into their elastic range, they will not hold, no matter how strong they are advertised.
Re: Torque To Yield
Some bolts are "torque to yield", and some are "torque plus angle". They're both usually called torque to yield. The 2nd article Kevin linked mentions LS chevy engines. It states the head bolts can't be reused, but rod and main bolts can. The head bolts are true torque to yield, but the main and rods are torque plus angle. There is a GM document about this, but I can't find it. I don't know which the Toyota bolts are. Like others said, I'd use old bolts for all checks until final assembly.
I used to be a people person, but people ruined it.
-
- Pro
- Posts: 414
- Joined: Sat Aug 23, 2008 7:12 am
- Location:
Re: Torque To Yield
As I expect most here know, using torque to achieve fastener stretch is notoriously variable due to inconsistent friction effects underhead and threads.
Yield point of a fastener is likely less variable. OEMs use this to optimize the bolted joint.
Local yield underhead is a guarantee in my opinion. Stress concentration in the radius is probably 3:1. Some stress concentration in the threads too.
Yield point of a fastener is likely less variable. OEMs use this to optimize the bolted joint.
Local yield underhead is a guarantee in my opinion. Stress concentration in the radius is probably 3:1. Some stress concentration in the threads too.
-
- Guru
- Posts: 1758
- Joined: Wed Aug 26, 2009 8:30 pm
- Location: Beautiful Southern Maryland
- Contact:
Re: Torque To Yield
Lewy,
There is an AERA bulletin that basically says you can reuse the bolts as long as they are not stretched and there is no thread damage. If you PM me your e-mail address I will send it to you or you can have your machine shop print it out for you. It is AERA TB 2141
There is an AERA bulletin that basically says you can reuse the bolts as long as they are not stretched and there is no thread damage. If you PM me your e-mail address I will send it to you or you can have your machine shop print it out for you. It is AERA TB 2141
Bill Koustenis
Advanced Automotive Machine
Waldorf Md
www.enginerepairshop.com
Advanced Automotive Machine
Waldorf Md
www.enginerepairshop.com
- BigBlockMopar
- Momentary Specialist
- Posts: 336
- Joined: Fri Mar 25, 2016 8:53 pm
- Location: Netherlands
- Contact:
Re: Torque To Yield
Here is a PDF link to that bulletin.
http://enginetechcatalog.com/images/Bul ... 202141.pdf
http://enginetechcatalog.com/images/Bul ... 202141.pdf
Re: Torque To Yield
Thank you everyone. BigBlockMopar thanks for the bulletin! I'm a bit less worried now. New factory bolts, measure them, check clearances, measure them again. I think that will tell me a little more.
Lewy
Lewy
-
- Pro
- Posts: 365
- Joined: Wed Nov 07, 2012 6:28 pm
- Location: Tallahassee Florida USofA
Re: Torque To Yield
They're fasteners that use the Torque-Angle method of tightening.
If they were TTY's, they'd look very different, with at least one if not more necked down narrow areas along the bolts length that do the Yield part of its name, stretching to near breaking and must not be re-used.
If they were TTY's, they'd look very different, with at least one if not more necked down narrow areas along the bolts length that do the Yield part of its name, stretching to near breaking and must not be re-used.
- midnightbluS10
- Expert
- Posts: 933
- Joined: Sun Oct 20, 2013 8:41 am
- Location: Shreveport, LA
Re: Torque To Yield
David Redszus wrote: ↑Wed Sep 11, 2019 10:52 am By definition, a bolt should be torqued into its elastic range but not into its plastic range.
If within its elastic range,the bolt should return to its original length. If it does not, it's use is
problematic.
Some OEMs will specify a used bolt critical dimension; either length or diameter, within which the bolt
may be reused. Lacking specifics, I find it useful to carefully measure and compare a new bolt to a used bolt.
Sometimes, the bolt stretch occurs in the threaded area which is more difficult to measure. Running a new nut down the bolt to test for thread binding can often indicate thread stretch.
Beware of using bolts that are too high in grade for the application. If they cannot be properly stretched into their elastic range, they will not hold, no matter how strong they are advertised.
I asked about measuring a different, new bolt to compare to a used bolt length. Useless unless you originally measured the length of the original bolt because not every bolt is the exact same length. I specifically asked Felpro about their TTY LS headbolts and that was their response.
In the end, I bought new bolts. It wasn't worth the risk. Bolts are cheap compared to a new engine. $60 ain't worth the hassle. Even on the stock rebuild of the I6 in my trailblazer, I used new bolts and those were like $90/set. It's not worth the risk to reuse $50 worth of bolts on a $10k engine, nor a $1000 engine, either.
JC -
bigjoe1 wrote:By the way, I had a long talk with Harold(Brookshire) last year at the PRI show. We met at the airport and he told me everything he knew about everything.It was a nice visit. JOE SHERMAN RACING
Re: Torque To Yield
Used bolts for checking, new bolts for assembly.
You may be able to figure out a torque value that you can for checking, if you do a lot of them.
You may be able to figure out a torque value that you can for checking, if you do a lot of them.
Re: Torque To Yield
I can't imagine anyone being able to measure the clearance difference between a main assembly torqued to a few lb-ft. less than yield vs. yield...
Felix, qui potuit rerum cognscere causas.
Happy is he who can discover the cause of things.
Happy is he who can discover the cause of things.